TYPE: BACK-UP & WORK ROLL
◆SUMMAY
It is made of high alloy steel melted with electroslag remelting furnace
and finished with forging and molten salt heat treatment
◆ADVANTAGE
◇High mechanical strength
◇Good toughness
◇High wearability
◇Excellent resistance to fire crack
◆PRODUCTS & APPLICATION
Material | Steel Grade | Chemical coposition % | Application | |||||||
C | Cr | Mo | V | Ni | Mn | Co | W | |||
Cr1 | GCr15 | 0.95 -1.05 | 1.3 -1.65 | ≤0.4 | Work roll of Cold mill Straightenning roll Pinch roll | |||||
9CrV | 0.85 -0.95 | 1.4 -1.7 | 0.1 -0.25 | ≤0.25 | ||||||
42CrMo | 0.38 -0.45 | 0.9 -1.2 | 0.15 -0.25 | Work roll
Backup roll for Hot rolling mill | ||||||
60CrMo | 0.55 -0.65 | 0.5 -0.8 | 0.3 -0.4 | |||||||
60CrMnMo | 0.55 -0.65 | 0.8 -1.2 | 0.3 -0.4 | 0.7 -1.0 | ||||||
60CrMoV | 0.55 -0.65 | 0.9 -1.2 | 0.3 -0.4 | 0.15 -0.35 | Straightenning roll Pinch roll | |||||
Cr2 | 9Cr2Mo | 0.85 -0.95 | 1.7 -2.1 | 0.2 -0.4 | Work roll,
Middle roll,
Backup roll for Cold Rolling mill | |||||
86CrMoV7 | 0.82 -0.9 | 1.8 -2.2 | 0.2 -0.4 | 0.1-0.2 | ||||||
9Cr2MoV | 0.85 -0.95 | 1.7 -2.1 | 0.2 -0.3 | 0.1-0.2 | ||||||
Cr3 | 9Cr3Mo | 0.85 -0.95 | 2.5 -3.5 | 0.2 -0.4 | Work roll,
Middle roll,
Backup roll for Cold Rolling mill (high quenching, deep hard layer) | |||||
MC3A | 0.8 -0.88 | 2.8 -3.2 | 0.4 -0.6 | 0.05 -0.12 | 0.6 -0.8 | |||||
MC3B | 0.82 -0.9 | 2.7 -3.1 | 0.1 -0.3 | 0.05 -0.12 | 0.2 -0.4 | |||||
70Cr3Mo | 0.6-0.75 | 2.0 -3.5 | 0.25 -0.6 | Work roll,
Middle roll,
Backup roll for Hot Rolling mill (high quenching, deep hard layer) | ||||||
70Cr3NiMo | 0.6 -0.8 | 2.0 -3.0 | 0.25 -0.6 | 0.4 -0.6 | ||||||
Cr5 | MC5 | 0.82 -0.9 | 5 -5.4 | 0.2 -0.4 | 0.1 -0.2 | 0.3 -0.5 | Work roll for Cold Rolling mill (high quenching, deep hard layer) | |||
MC5A | 0.77 -0.84 | 5 -5.4 | 0.3 -0.5 | 0.1 -0.2 | 0.3 -0.5 | |||||
Cr12 | Cr12MoV | 1.45 -1.7 | 11 -12.5 | 0.4 -0.6 | 0.15 -0.3 | Work roll,
Middle roll for Multi-roll Rolling mill | ||||
Cr12Mo1V1 | 1.4 -1.6 | 11 -13 | 0.7 -1.2 | ≤1.1 | ≤1.0 | |||||
Cr12MoVCo | 1.4 -1.6 | 11 -13 | 0.8 -1.2 | 0.75 -0.95 | 0.3 -0.5 | |||||
W steel | W6Mo5Cr4V2 | 0.8 -0.9 | 3.8 -4.0 | 4.5 -5.5 | 1.75 -2.25 | 5.5 -6.75 | Work roll for Multi-roll Rolling mill | |||
W12Cr4V5Co5 | 1.5 -1.6 | 3.75 -5.0 | ≤1.0 | 4.5 -5.25 | 4.75 -5.25 | 11.75 -13 |